Fiberglass Woven Fabric (Yarn)
Product features | Applications |
Good compatibility with UP, VE and EP resins High Mechanical strength Good structural stability Beautiful surface | Shipbuilding industry Sprots equipment Military Automobile industry |
Fiberglass Woven Fabric (Yarn) Specification List
Code | Structure | Density (root/cm) | Weight (g/㎡) | Tensile strength (N/25mm) | Yarn number (Tex) | Yarn/roving Diameter (um) | |||
Warp | Weft | Warp | Weft | Warp | Weft | ||||
EW30 | Plain | 20±2 | 18±2 | 23±2 | ≥160 | ≥70 | 8 | 4 | 4.5 |
EW60 | Plain | 20±2 | 20±2 | 48±4 | ≥260 | ≥260 | 12.5 | 12.5 | 5.5 |
EW80 | Plain | 12±1 | 12±1 | 80±8 | ≥300 | ≥300 | 33 | 33 | 9 |
EWT80 | Twill | 12±2 | 12±2 | 80±8 | ≥300 | ≥300 | 33 | 33 | 9 |
EW100 | Plain | 16±1 | 15±1 | 110±10 | ≥400 | ≥400 | 33 | 33 | 9 |
EWT100 | Twill | 16±1 | 15±1 | 110±10 | ≥400 | ≥400 | 33 | 33 | 9 |
EW120 | 4-HS | 23.62 | 22.83 | 107 | ≥690 | ≥690 | 11 | 11 | 5 |
EW130 | Plain | 10±1 | 10±1 | 130±10 | ≥600 | ≥600 | 66 | 66 | 9 |
EW160 | Plain | 12±1 | 12±1 | 160±12 | ≥700 | ≥650 | 66 | 66 | 9 |
EWT160 | Twill | 12±1 | 12±1 | 160±12 | ≥700 | ≥650 | 66 | 66 | 9 |
EW200 | Plain | 8±0.5 | 7±0.5 | 198±14 | ≥650 | ≥550 | 132 | 132 | 9 |
EW200 | Plain | 16±1 | 13±1 | 200±20 | ≥700 | ≥650 | 66 | 66 | 9 |
EWT200 | Twill | 16±1 | 13±1 | 200±20 | ≥900 | ≥700 | 66 | 66 | 9 |
EW300 | Plain | 8±0.5 | 7±0.5 | 300±24 | ≥1000 | ≥800 | 200 | 200 | 13 |
EWT300 | Twill | 8±0.5 | 7±0.5 | 300±24 | ≥1000 | ≥800 | 200 | 200 | 13 |
EW400 | Plain | 8±0.5 | 7±0.5 | 400±32 | ≥1200 | ≥1100 | 264 | 264 | 13 |
EWT400 | Twill | 8±0.5 | 7±0.5 | 400±32 | ≥1200 | ≥1100 | 264 | 264 | 13 |
EW400 | Plain | 6±0.5 | 6±0.5 | 400±32 | ≥1200 | ≥1100 | 330 | 330 | 13 |
EWT400 | Twill | 6±0.5 | 6±0.5 | 400±32 | ≥1200 | ≥1100 | 330 | 330 | 13 |
Fiberglass Woven Fabric (Roving)
Product features | Applications |
Excellent laminate properties and costeffective reinforcement. Ease of handling and drapability. Rapid wet-out and fast application. Design flexibility and engineered strain values. High-impact response | Hand lay-up and robot, processes to manufacture boats, vessels, plane and automotive parts, furniture and sports facilities |
Fiberglass Woven Fabric (Roving) Specification List
Produce No | Glass | Weight(g/m2) | Breaking Strength ≥N/25MM | Weave | Moisture Content% | L.O.I Content% | |
Warp | Weft | ||||||
EWR200 | E | 200+/-10 | 820 | 700 | Plain | ≤0.1 | 0.4-0.8 |
EWR200B | E | 200+/-10 | 820 | 700 | Plain | ≤0.1 | 0.4-0.8 |
EWR270 | E/ECR | 270+/-14 | 1200 | 1000 | Plain | ≤0.1 | 0.4-0.8 |
EWR300 | E | 300+/-15 | 1200 | 1200 | Plain | ≤0.1 | 0.4-0.8 |
EWR300TM | E | 300+/-15 | 1500 | 900 | Plain | ≤0.1 | 0.4-0.8 |
EWR300B | E | 300+/-15 | 1200 | 1250 | Plain | ≤0.1 | 0.4-0.8 |
EWR360 | E/ECR | 360+/-18 | 1200 | 1150 | Plain | ≤0.1 | 0.4-0.8 |
EWR400 | E | 400+/-20 | 1480 | 1380 | Plain | ≤0.1 | 0.4-0.8 |
EWR400TM | E | 400+/-20 | 1500 | 1500 | Plain | ≤0.1 | 0.4-0.8 |
EWR400B | E | 325+/-16 | 1200 | 1380 | Plain | ≤0.1 | 0.4-0.8 |
EWR500 | E | 500+/-25 | 1800 | 1700 | Plain | ≤0.1 | 0.4-0.8 |
EWR500T | E | 500+/-25 | 1800 | 1600 | Twill | ≤0.1 | 0.4-0.8 |
EWUDT500 | E | 500+/-25 | 100 | 2900 | Plain | ≤0.1 | 0.4-0.8 |
EWUDL500 | E | 500+/-25 | 2600 | 350 | Plain | ≤0.1 | 0.4-0.8 |
EWUDL530 | E | 530+/-27 | 3200 | 800 | Plain | ≤0.1 | 0.4-0.8 |
EWR580 | E/ECR | 580+/-29 | 1900 | 1600 | Plain | ≤0.1 | 0.4-0.8 |
EWR600 | E | 600+/-30 | 1900 | 1800 | Plain | ≤0.1 | 0.4-0.8 |
EWR600B | E | 600+/-30 | 1900 | 1850 | Plain | ≤0.1 | 0.4-0.8 |
EWUDL600 | E | 600+/-30 | 3100 | 350 | Plain | ≤0.1 | 0.4-0.8 |
EWR800 | E | 800+/-40 | 2600 | 2300 | Plain | ≤0.1 | 0.4-0.8 |
EWR800A | E | 864+/-43 | 2900 | 2700 | Plain | ≤0.1 | 0.4-0.8 |
EWR1000 | E | 1000+/-50 | 2900 | 2900 | Plain | ≤0.1 | 0.4-0.8 |